Durable Top Quality 4X8 7075 Aluminum Sheet for Aircraft

• Application: Transportation Tools, Door & Window, Glass Wall, Heat Sink, Decorations, Mold Tool Manufacturing, Aircraft Structure
• Certification: RoHS, ISO9001, ASTM, JIS, GB, EN, ASTMB
• Technique: Extruded
• Grade: 7000 Series
• Temper: T351 - T651
• Surface Treatment: Mill Finish
• Model NO.: 7075
• Alloy: Alloy
• Thickness: 0.1mm to 400mm
• Width: 1000mm to 2200mm
• Length: up to 6 Meters
• Tolerance: +/-0.02mm
• Mtc: En 10204/3.1
• Standard: ASTM B209, ISO 6361, En573-1 etc.
• Transport Package: as Customer′s Requirement
• Trademark: ZYTC
• Origin: China
• HS Code: 76042990
• Production Capacity: 500 Tons/Month

Product Description

1: Product Details

7075 aluminum sheet is a high-strength material that is commonly used in aerospace and defense applications due to its excellent strength-to-weight ratio. ZYTC, a leading manufacturer of aluminum products, produces high-quality 7075 aluminum sheet that is highly sought after in the industry.

The properties of 7075 aluminum sheet make it an ideal choice for a wide range of applications. It has excellent fatigue resistance, which means it can withstand repeated stress without cracking or failing. This makes it perfect for use in critical components of aircraft, such as wing structures and landing gear.

In addition to its exceptional strength, 7075 aluminum sheet also has good machinability and weldability, making it easy to work with during manufacturing processes. It is also corrosion-resistant, which ensures that it will maintain its strength and integrity over time.

ZYTC's 7075 aluminum sheet is manufactured using state-of-the-art equipment and techniques that ensure consistent quality and precision. The company uses advanced technology to produce aluminum sheets that meet the highest standards of strength, durability, and performance.

One of the unique features of ZYTC's 7075 aluminum sheet is its ability to be heat-treated and strengthened even further. This process involves heating the material to a specific temperature and then quenching it in water or oil. The resulting product is stronger and more durable than the original material, making it ideal for use in high-stress applications.

Overall, ZYTC's 7075 aluminum sheet is an excellent choice for those in need of a high-strength, lightweight material for their aerospace or defense project. Its superior strength, excellent fatigue resistance, and corrosion resistance make it a reliable and cost-effective option for a wide range of applications. With ZYTC's commitment to quality and precision, you can trust that their 7075 aluminum sheet will meet your needs and exceed your expectations.

Mechanical properties:
The mechanical properties of 7075 depend greatly on the temper of the material.
7075-O
Un-heat-treated 7075 (7075-O temper) has maximum tensile strength no more than 280 MPa (40,000 psi), and maximum
yield strength no more than 140 MPa (21,000 psi). The material has an elongation (stretch before ultimate failure) of 9-10%.
It is very highly corrosion-resistant and has good strength.
7075-T6
T6 temper 7075 has an ultimate tensile strength of 510-540 MPa (74,000-78,000 psi) and yield strength of at least 430-480 MPa .
It has a failure elongation of 5-11%.The T6 temper is usually achieved by homogenizing the cast 7075 at 450°C for several hours,
quenching, and then aging at 120 °C for 24 hours. This yields the peak strength of the 7075 alloy. The strength is derived mainly
from finely dispersed eta and eta' precipitates both within grains and along grain boundaries.
7075-T651
T651 temper 7075 has an ultimate tensile strength of 570 MPa (83,000 psi) and yield strength of 500 MPa (73,000 psi). It has a
failure elongation of 3-9%. These properties can change depending on the form of material used. Thicker plate may exhibit lower
strengths and elongation than the numbers listed above.
7075-T7
T7 temper has an ultimate tensile strength of 505 MPa (73,200 psi) and a yield strength of 435 MPa (63,100 psi). It has a failure
elongation of 13%.T7 temper is achieved by overaging (meaning aging past the peak hardness) the material. This is often
accomplished by aging at 100-120 °C for several hours and then at 160-180 °C for 24 hours or more. The T7 temper produces
a micro-structure of mostly eta precipitates. In contrast to the T6 temper, these eta particles are much larger and prefer growth
along the grain boundaries. This reduces the susceptibility to stress corrosion cracking. T7 temper is equivalent to T73 temper.
Due to its high strength, low density, thermal properties, and its ability to be highly polished, 7075 is widely used in mold tool
manufacturing. This alloy has been further refined into other 7000 series alloys for this application, namely 7050 and 7020.

2: Chemical Composition  


Aluminum Grades:
1000 series: 1035,1040,1050,1060,1070,1080,1090,1098,1100,1230,1435,1260,1170,1275,1285,1385
2000 series: 2001,2002,2011,2014,2017,2117,2218,2519,2024,2224,2025,2030,2031,2036,2090,2091
3000 series: 3002,3003,3004,3103,3203,3303,3105,3006,3007,3107,3008,3009,3015,3016
5000 series: 5005,5205,5006,5010,5013,5014,5016,5017,5040,5043,5050,5150,5251,5351,5451,5052,5083
                   5352,5552,5254,5754,5856,5456,5283
6000 series: 6101,6201,6003,6103,6105,6205,6006,6106,6110,6061,6060,6063,6863,6081,6082,6162,6863
7000 series: 7001,7003,7005,7108,7129,7146,7050,7472,7075,7076,7277,7178,7278,7091,7277
8000 series: 8001,8004,8006,8011,8111,8014,8030,8130,8177,8079,8081,8280,8091

Aluminum Temper:
O,H12,H13,H14,H16,H18,H24,H32,H34,H19,H38,G36,F,H111,H112,H192,H392,H393,H321
T1,T3,T4,T8,T72,T451,T42,T62,T5,T6,T36,T351,T651,T851,T3511,T913,T94,T7351,T89,T4510,