spring Tempered Full Hard 301 Stainless Steel Sheet Price Per Kg

• Type: Steel Plate
• Standard: ASTM, AISI, GB, JIS, DIN, BS
• Certification: ISO, RoHS, IBR
• Surface Treatment: Ba, Hl, 8k, Sb, 2b, No.1, 1d
• Technique: Hot Rolled, Cold Rolled
• Special Use: Springs, Truck and Trailer Bodies
• Model NO.: 301
• Stock: Stock
• Width: 1000mm to 2200mm
• Length: Cut as Requirement
• Edge: Mill Edge or Slit Edge
• Mtc: En 10204/3.1
• Transport Package: as Customer′s Requirement
• Specification: Thickness 0.3mm to 280mm
• Trademark: ZYTC
• Origin: China
• HS Code: 72192100
• Production Capacity: 500 Tons/Month

Product Description

1: Product Details:

301 stainless steel an austenitic stainless with excellent corrosion resistance. Precision Steel stocks 301 stainless steel in the
1/4 hard, 1/2 hard, 3/4 hard, full hard, and extra hard tempers.
Stainless steel 301 is known for its high strength and excellent corrosion resistance. Alloy 301 is non-magnetic when annealed
however it has the ability to be modified along with its other properties. Because of the versatility of this grade of stainless steel,
it makes 301 stainless steel the ideal material for a multitude of applications.
Stainless steel grade 301 and low carbon variants of this grade are predominantly used as high strength stainless steel.
The work hardening rates of these grades are very high, in the range of a 14MPa increase per 1% reduction in area of cold work.
As a result of this characteristic high strength can be achieved from cold rolling and roll forming operations.
Through such forming methods strain hardened austenite may be partially transformed to martensite. In spite of achieving such
high strengths, the residual ductility in the alloy is capable of causing severe cold deformation. The alloy is non-magnetic in the
annealed condition, but shows strong magnetism when cold worked.
301 is suitable for all forms of standard welding methods. The use of grade 308L as filler metal is recommended.
Welded parts in grade 301 must be subjected to annealing in order to attain maximum corrosion resistance.
For grades 301L and 301LN annealing is not necessary after welding. The purpose of welding followed by annealing is to
remove the high strength brought about by cold rolling.

2:Chemical Composition with different standards:

Tianjin Zhongyantiancheng Steel Co.,Ltd
Commodity	Stainless Steel Plate/Stainless Steel Sheet
Material	301
Standard	GB	JIS	ASTM/ASME	DIN
	12Cr17Ni7	SUS301	301	1.4319
Chemical Composition	C	Mn	P	S
	<=0.15	<=2	<=0.045	<=0.03
	Si	Cr	N	Ni
	<=1	16-18	<=0.1	6-8
Thickness	0.3mm--16mm(cold rolled) 3mm--280mm(hot rolled)
Width	1000mm--2200mm
Length	1000mm-6000mm, as customers' request
Surface	BA/2B/NO.1/NO.3/NO.4/8K/HL/2D/1D
manufacture	Hot Rolled/Cold Rolled
Packing	Packed in bundles with standard export sea-worthy package
Delivery Time	Within 15 working days, according to customers' quantities
Quality	High Quality.SGS inspection is accepted if needed
Place of Origin	Tianjin
Productivity	500 MT/Month
Payment	T/T,L/C
MOQ	1 MT
Application	automobile molding and trim, wheel cover, conveyor belts, kitchen equipment, roof draining systems
Note	We can also do other materials