1mm 2mm 3mm 0.5mm Thickness Super Hard 301 Stainless Steel Strip Coil

• Type: Stainless Steel Coil
• Standard: ASTM, AISI, GB, JIS, DIN, EN
• Grade: 300 Series
• Certification: ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS
• Shape: Round
• Technique: Hot Rolled, Cold Rolled
• Model NO.: 301
• Surface Treatment: 2b, Ba, Hl. No.1
• Thickness: 0.3mm to 16mm
• Width: 1000*C/1220*C/1250*C/1500*C/1540*C/1800*C/2000*C
• Edge: Mill Edge or Slit Edge
• Mtc: En 10204/3.1
• Surface: 2b, No.1, 1d, 2D, Hl, 8K, Ba, Sb
• Stock or Not: Large Stock
• Transport Package: as Customer′s Requirement
• Trademark: ZYTC
• Origin: China
• HS Code: 72192100
• Production Capacity: 500 Tons/Month

Product Description

1: Brief Introduction Of 301 stainless steel strip
 301 stainless steel is an austenitic stainless with excellent corrosion resistance. Precision Steel stocks 301 stainless steel
in the, 1/4 hard, 1/2 hard, 3/4 hard, full hard, and extra hard tempers.
Stainless steel 301 is known for its high strength and excellent corrosion resistance. Alloy 301 is non-magnetic when annealed
however it has the ability to be modified along with its other properties. Because of the versatility of this grade of stainless steel,
it makes 301 stainless steel the ideal material for a multitude of applications.Stainless steel grade 301 and low carbon variants
of this grade are predominantly used as high strength stainless steel. The work hardening rates of these grades are very high,
in the range of a 14MPa increase per 1% reduction in area of cold work. As a result of this characteristic high strength can be
achieved from cold rolling and roll forming operations.
Through such forming methods strain hardened austenite may be partially transformed to martensite. In spite of achieving such
high strengths, the residual ductility in the alloy is capable of causing severe cold deformation. The alloy is non-magnetic in the
annealed condition, but shows strong magnetism when cold worked.
301 is suitable for all forms of standard welding methods. The use of grade 308L as filler metal is recommended. Welded parts
in grade 301 must be subjected to annealing in order to attain maximum corrosion resistance. For grades 301L and 301LN
annealing is not necessary after welding.
The purpose of welding followed by annealing is to remove the high strength brought about by cold rolling.
2: Chemical Composition

Tianjin Zhongyantiancheng Steel Co.,Ltd
Commodity	Stainless Steel Coil/Stainless Steel Roll
Material	301
Standard	GB	JIS	ASTM/ASME	DIN
	12Cr17Ni7	SUS301	301	1.4319
Chemical Composition	C	Mn	P	S
	<=0.15	<=2	<=0.045	<=0.03
	Si	Cr	N	Ni
	<=1	16-18	<=0.1	6-8
Thickness	0.3mm--6mm(cold rolled) 3mm--16mm(hot rolled)
Width	1000mm--2200mm
Surface	BA/2B/NO.1/NO.3/NO.4/8K/HL/2D/1D
manufacture	Hot Rolled/Cold Rolled
Packing	Packed in bundles with standard export sea-worthy package
Delivery Time	Within 15 working days, according to customers' quantities
Quality	High Quality.SGS inspection is accepted if needed
Place of Origin	Jiangsu
Productivity	500 MT/Month
Payment	T/T,L/C
MOQ	1 MT
Application	automobile molding and trim, wheel cover, conveyor belts, kitchen equipment, roof draining systems
Note	We can also do other materials