ASTM B234 Drawn 5083/5052 Aluminum Pipe for Heat Exchanger Used

• Customization: Available
• Shape: Square
• Surface Treatment: Anodized,Mill Finished,Polished,Sand Blasted,Brush
• Model NO.: 5052, 5083
• Alloy: Non-alloy
• Temper: O - H112
• Outside Diameter: 2.5mm to 560mm
• Thickness: 0.2mm to 60mm
• Length: Cut as Requirement
• Mtc: En 10204/3.1
• Standard: ASTM B210,B221,B483,B491,B547 etc.
• Color: Cream White, Anodized, Natural Finish
• Keyword: 5052 Aluminum Alloy Pipe
• Transport Package: as Customer′s Requirement
• Trademark: ZYTC
• Origin: China
• HS Code: 7608201010
• Production Capacity: 500 Tons/Month

Product Description

Aluminium / Aluminum 5052 alloy is a non-heat treatable alloy with good corrosion resistance, especially to salt water.
The following datasheet will provide more details about Aluminium / Aluminum 5052 alloy.
Machinability:
The machinability of Aluminium / Aluminum 5052 alloy is rated as fair. This alloy can be easily machined in hard temper
than in annealed form, and the quality of finish is better. Other than in very light cuts, all other machining should be done
using oil lubricants.
Forming:
Aluminium / Aluminum 5052 alloy can be easily formed at room temperature. However, consecutive cold working tends to
reduce the alloy's formability
Welding:
Welding can be easily performed on Aluminium / Aluminum 5052 alloy using conventional methods. In case a filler rod is
needed, it should be Aluminium / Aluminum 5356 alloy as filler. The most suitable welding methods are tungsten or consumable
electrode inert gas shielded arc welding.
Forging:
Aluminium / Aluminum 5052 alloy can be forged from 510°C (950°F) down to 260°C (500°F).
Hot Working:
Aluminium / Aluminum 5052 alloy can be hot worked easily from 510°C (950°F) down to 260°C (500°F).
Cold Working:
Aluminium / Aluminum 5052 alloy is easy to cold work. It can be formed by spinning and drawing. Depending on the
extent of spinning, annealing may be required intermediately.
Annealing:
Aluminium / Aluminum 5052 alloy can be annealed at 343°C (650°F) and then air cooled.
Hardening:
Aluminium / Aluminum 5052 alloy can be hardened by cold working only.
Applications:
Aluminium / Aluminum 5052 alloy is used in the manufacture of the following products:
Milk crates
Hydraulic tubes
Appliances
Kitchen cabinets
Small boats home freezers
Aircraft tube
Fencing
This alloy is also used widely in sheet metal work and in sheet metal parts.

Chemical Composition 


Aluminum Grades:
1000 series: 1035,1040,1050,1060,1070,1080,1090,1098,1100,1230,1435,1260,1170,1275,1285,1385
2000 series: 2001,2002,2011,2014,2017,2117,2218,2519,2024,2224,2025,2030,2031,2036,2090,2091
3000 series: 3002,3003,3004,3103,3203,3303,3105,3006,3007,3107,3008,3009,3015,3016
5000 series: 5005,5205,5006,5010,5013,5014,5016,5017,5040,5043,5050,5150,5251,5351,5451,5052,5083
             5352,5552,5254,5754,5856,5456,5283
6000 series: 6101,6201,6003,6103,6105,6205,6006,6106,6110,6061,6060,6063,6863,6081,6082,6162,6863
7000 series: 7001,7003,7005,7108,7129,7146,7050,7472,7075,7076,7277,7178,7278,7091,7277
8000 series: 8001,8004,8006,8011,8111,8014,8030,8130,8177,8079,8081,8280,8091

Aluminum Temper:
O,H12,H13,H14,H16,H18,H24,H32,H34,H19,H38,G36,F,H111,H112,H192,H392,H393,H321
T1,T3,T4,T8,T72,T451,T42,T62,T5,T6,T36,T351,T651,T851,T3511,T913,T94,T7351,T89,T4510,T6510,T8510,
T8511,T4511,T52,T5511,T6511,T54,T73

The aluminum industry has created a system using a four-digit numerical designation to identify wrought aluminum alloys.  
The first digit indicates the major alloying element.  The second digit indicates whether there was a modification in the basic alloy.  
The third and fourth digit indicates the specific alloy.  The following represent the various groups:

1XXX	Aluminum 99% or greater
2XXX	Copper - major alloying element
3XXX	Manganese - major alloying element
5XXX	Magnesium - major alloying element
6XXX	Magnesium and silicon - major alloying elements
7XXX	Zinc -major alloying element

Aluminium/Aluminum Alloy Process

Aluminium/Aluminum Alloy Pipe Package