| Color: | Mill Finish |
|---|---|
| Application: | Transportation Tools, Door & Window, Glass Wall, Heat Sink, Decorations, Pressure Vessels, Marine Service and Structures |
| Certification: | RoHS, ISO9001, ASTM, JIS, GB, EN, ASTMB |
| Technique: | Extruded |
| Grade: | 5000 Series |
| Temper: | O - H112 |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
5454 aluminium alloy is an alloy in the wrought aluminium-magnesium family (5000 or 5xxx series). It is closely
related to 5154 aluminium alloy. As an aluminium-magnesium alloy, it combines moderate-to-high strength with
excellent weldability. Like 5154, 5454 aluminium is commonly used in welded structures such as pressure vessels
and ships. As a wrought alloy, it can be formed by rolling, extrusion, and forging (although forging is not common),
but not casting. It can be cold worked to produce tempers with a higher strength but a lower ductility. It is generally not clad.
Annealing:
Aluminium / Aluminum 5454 alloy is annealed at 343°C (650°F) only when the need to relieve the cold working stress
arises. After being sufficiently heated the alloy is finally cooled in air.
Cold Working:
Aluminium / Aluminum 5454 alloy is capable of being cold worked by using conventional methods. This alloy can be cold
worked in any of the H-32, H-34, H-111 tempers or in the annealed condition.
Welding:
Aluminium / Aluminum 5454 alloy is capable of being welded by all the commercial welding methods.
Forging:
Aluminium / Aluminum 5454 alloy can be hot forged.
Forming:
Aluminium / Aluminum 5454 alloy can be readily cold worked in the annealed or tempered conditions. This alloy
contains good cold working and hot working characteristics.
Machinability:
The machinability of Aluminium / Aluminum 5454 alloy is rated from fair to poor. Machining operations for this alloy is
recommended when the alloy is in the H-34 temper condition. Oil lubricants can be used in the machining process.
Heat Treatment:
Aluminium / Aluminum 5454 alloy cannot be heat treated.
Hot Working:
Aluminium / Aluminum 5454 alloy can be hot worked in the temperature range of 371 to 204°C (700 to 400°F).
Hardening:
Aluminium / Aluminum 5454 alloy can be hardened only by being cold worked.
Applications:
Aluminium / Aluminum 5454 alloy is used in pressure vessels, marine service and welded structures.