Corrosion-Resistant Nimo16cr15W 2.4819 Hastelloy C276 Nickel Alloy Plate for Flue Gas Equipment

• Customization: Available
• Application: Aviation, Electronics, Industrial, Medical, Chemical
• Standard: JIS, GB, DIN, ASTM, AISI
• Model NO.: hastelloy C276
• Purity: 36%
• Alloy: Alloy
• Type: Nickel Plate
• Powder: Not Powder
• Finish: 2b/No.1/1d/2D/Ba/Sb/Hl/No.4/No.8
• Color: Customized
• Edge: Mill Edge/Slit Edge
• Mtc: En 10204/3.1
• MOQ: 500 Kg
• Trade Terms: Fob CIF CFR EXW etc
• Stock: in Stock
• Length: as Your Requirments
• Keywords: Ss Sheet Cut to Size
• Transport Package: Wooden Package
• Specification: 0.3~6mm
• Trademark: ZYTC
• Origin: China
• HS Code: 7219900000
• Production Capacity: 100tons; 200tons/Month

Product Description

 

 

Product Name	Corrosion-Resistant  NiMo16Cr15W 2.4819 Hastelloy C276 Nickel Alloy Plate for Flue Gas Equipment
Thickness	0.3mm-200mm
Width	1000mm-4000mm
Length	2000 mm , 2438 mm , 3000 mm , 6000 mm OR as reqirement
Finish	No.1 , 2B , HL , NO.4 , BA , SB ,1D , 2D , 2C , 2E , NO.5 , NO.9
Technical	Hot rolling,Cold rolling
Standard	ASTM B536
MOQ	100 KG for production, 1PC for stock
Certification	MTC Type 3.1 , PMI , CO
Delivery Time	7 days if have stock

 What is Alloy C276?

Introduction

Super alloys or high performance alloys are available in a variety of shapes and contain elements in different combinations to obtain a specific result. These alloys are of three types that include iron-based, cobalt-based and nickel-based alloys. The nickel-based and cobalt-based super alloys are available as cast or wrought based alloys according to composition and application.

Super alloys have good oxidation and creep resistance and can be strengthened by precipitation hardening, solid-solution hardening and work hardening methods. They can also function under high mechanical stress and high temperatures and also in places that require high surface stability.

HASTELLOY C276 is a wrought corrosion-resistant alloy that resists the development of grain boundary precipitates that degrade corrosion resistance.

The following datasheet provides an overview of HASTELLOY C276.

Shape	Round,Forging,Ring,Coil,Flange,Disc,Foil,Spherical,Ribbon,Square,Bar,Pipe,Sheet
Grade	Duplex: 2205(UNS S31803/S32205),2507(UNS S32750),UNS S32760(Zeron 100),2304,904L
	Others:253Ma,254SMo,654SMo,F50(UNSS32100)F60,F61,F65,1J22,N4,N6 etc
	Alloy : Alloy 20/28/31
	Hastelloy:HastelloyB/ -2/B-3/C22/C-4/S/ C276/C-2000/G-35/G-30/X/N/g
	Hastelloy B / UNS N10001,Hastelloy B-2 / UNS N10665 / DIN W. Nr. 2.4617,Hastelloy C, Hastelloy C-4 / UNS N06455 / DIN W. Nr. 2.4610,Hastelloy C-22 / UNS N06022 / DIN W. Nr. 2.4602, Hastelloy C-276 / UNS N10276 / DIN W. Nr. 2.4819,Hastelloy X / UNS N06002 / DIN W. Nr. 2.4665
	Haynes: Haynes 230/556/188
	Inconel 600/601/602CA/617/625/713/718/738/X-750,Carpenter 20
	Inconel 718 / UNS N07718 / DIN W. Nr. 2.4668,Inconel 601 / UNS N06601 / DIN W. Nr. 2.4851, Inconel 625 / UNS N06625 / DIN W. Nr. 2.4856,Inconel 725 / UNS N07725,Inconel X-750 / UNS N07750 / DIN W. Nr. 2.4669,Inconel 600 / UNS N06600 / DIN W. Nr. 2.4816
	Incoloy: Incoloy 800/800H/800HT/825/925/926;
	GH: GH2132,GH3030,GH3039,GH3128,GH4180,GH3044
	Monel: Monel 400/K500/R405
	Nitronic: Nitronic 40/50/60;
	Nimonic: Nimonic 75/80A/90/A263 ;
Specification	Wire: 0.01-10mm Strip: 0.05*5.0-5.0*250mm  Bar: φ4-50mm;Length 2000-5000mm Pipe: φ6-273mm;δ1-30mm;Length 1000-8000mm Sheet: δ 0.8-36mm;Width 650-2000mm;Length 800-4500mm

Chemical Composition

The chemical composition of HASTELLOY C276 is outlined in the following table.

Element	Content (%)
Nickel, Ni	57
Molybdenum, Mo	15-17
Chromium, Cr	14.5-16.5
Iron, Fe	4-7
Tungsten, W	3-4.50
Cobalt, Co	2.50
Manganese, Mn	1
Vanadium, V	0.35
Silicon, Si	0.080
Phosphorous, P	0.025
Carbon, C	0.010
Sulfur, S	0.010

Physical Properties

The following table shows the physical properties of HASTELLOY C276.

Properties	Metric	Imperial
Density	8.89 g/cm³	0.321 lb/in³
Melting point	1371°C	2500°F

Mechanical Properties

The mechanical properties of HASTELLOY C276 are displayed in the following table.

Properties	Metric	Imperial
Tensile strength (@thickness 4.80-25.4 mm, 538°C/@thickness 0.189-1.00 in, 1000°F)	601.2 MPa	87200 psi
Yield strength (0.2% offset, @thickness 2.40 mm, 427°C/@thickness 0.0945 in, 801°F)	204.8 MPa	29700 psi
Elastic modulus (RT)	205 GPa	29700 ksi
Elongation at break (in 50.8 mm, @thickness 1.60-4.70 mm, 204°C/@thickness 0.0630-0.185 in, 399°F)	56%	56%
Hardness, Rockwell B (plate)	87	87

Thermal Properties

The thermal properties of HASTELLOY C276 are given in the following table.

Properties	Metric	Imperial
Thermal expansion co-efficient (@24-93°C/75.2-199°F)	11.2 µm/m°C	6.22 µin/in°F
Thermal conductivity (-168 °C)	7.20 W/mK	50.0 BTU in/hr.ft².°F

Other Designations

Equivalent materials to HASTELLOY C276 are as follows.

ASTM B366	ASTM B574	ASTM B622	ASTM F467	DIN 2.4819
ASTM B575	ASTM B626	ASTM B619	ASTM F468

Fabrication and Heat Treatment

Annealing

 

HASTELLOY C276 is generally used in the solution treated condition. This alloy is soaked at 1121°C (2050°F) and then quenched in a rapid manner.

Cold Working

Conventional cold working procedures are used for cold working HASTELLOY.

Welding

HASTELLOY C276 is capable of being welded by the commonly used welding methods. During the welding process excessive input of heat should be avoided. For corrosive applications this alloy is capable of being used in the "as-welded" condition without the need for more heat treatment.

Forging

Conventional methods are used to forge or hot-upset HASTELLOY C276.

Forming

HASTELLOY C276 can be formed by being cold worked using conventional techniques.

Machinability

HASTELLOY C276 has good machinability characteristic.

Heat Treatment

HASTELLOY C276 is solution heat treated at 1121°C (2050°F) and then quenched rapidly. In case of forging or hot forming, the parts should first be solution heat treated before usage.

Hardening

HASTELLOY C276 is cold worked to be hardened.

Hot Working

Super alloy HASTELLOY C276 is capable of being extruded or hot formed. After the hot forming process, this alloy should be solution heat treated.

Aging

Aging is not performed for HASTELLOY C276 that is utilized in a solution treated condition.

Applications

HASTELLOY C276 is used for desulphurization of flue gas equipment and for chemical process equipment.

 

Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .

Q2: Can I have free sample before making orders?

A2: Yes,we can supply free sample as requirement,but buyer needs to pay the freight charges ,the freight fee will return to buyer after making order.

Q3: How do you control the quality ?
A3: MTC and PMI will be sent before shipment,any 3rd party inspection if need .

Q4: How about your delivery time ?
A4: Generally delivery time is 15 working days .

Q5: How can I quickly get the price list ?
A5: Directly click "chat now" or send us email with detail specifications,you will get the official price list in 1 hour .