Aluminium / Aluminum 5005 alloy is a non-heat treatable alloy with small amount of magnesium content. It has
excellent corrosion resistance and weldability characteristics. The following datasheet will provide more details about
Aluminium / Aluminum 5005 alloy.
Machinability
Aluminium / Aluminum 5005 alloy has poor machinability in the soft temper conditions. However, the alloy can be machined,
but is a lot tougher than many of the other aluminum alloys. The alloy in the harder tempers such as H34 and H38 can be
machined better than the alloy in the soft temper condition.
Forming:
Formability of Aluminium / Aluminum 5005 alloy, especially in the softer tempers, can be easily achieved using
conventional methods.
Welding:
Aluminium / Aluminum 5005 alloy has excellent welding capacity. Welding is possible using all the commercial methods.
Filler metal of the same alloy has to be used. Welding using resistance method of the O or annealed temper material
requires some trial and error determination.
Heat Treatment:
Aluminium / Aluminum 5005 alloy cannot be heat treated, except when annealed to minimize cold working strain.
Forging:
Aluminium / Aluminum 5005 alloy is forgeable.
Hot Working:
Aluminium / Aluminum 5005 alloy does not require hot working in most cases. But if it is required the preferable temperature
range is 371 to 204°C (700 to 400°F).
Cold Working:
Aluminium / Aluminum 5005 alloy has excellent cold working capacity including the harder tempers.
Annealing:
Annealing can be performed at 343°C (650°F) if required. This should be followed by air cooling.
Hardening:
Aluminium / Aluminum 5005 alloy can be hardened only by cold working.
Applications:
Aluminium / Aluminum 5005 alloy is widely used in the manufacture of the following products:
Small boats
Appliances
Utensils
Gas lines
Refrigerator panels
Fresh and salt water
The 5005 alloy can also used in architectural parts and as an electrical conductor. It is very useful to avoid excessive finishing
costs when using the 3003 alloys due to surface roughness while drawing
| 1XXX | Aluminum 99% or greater |
| 2XXX | Copper - major alloying element |
| 3XXX | Manganese - major alloying element |
| 5XXX | Magnesium - major alloying element |
| 6XXX | Magnesium and silicon - major alloying elements |
| 7XXX | Zinc -major alloying element |