| Type: | Stainless Steel Pipes |
|---|---|
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
| Grade: | Duplex Stainless Steel |
| Certification: | ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS |
| Shape: | Round.Square.Rectangle |
| Technique: | Hot Rolled/Cold Drawing/Pickling/Precision Rolling |
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
| Product Name | ASTM A879 S32707 2707 1.4658 Duplex Stainless Steel Seamless Pipe |
| Thickness | 0.5 mm - 68 mm SCH10, SCH20, SCH30, STD, SCH40, SCH60, SCH80, SCH100 SCH120, SCH160, XS, XXS |
| Outside Diameter | 4 mm -1500 mm |
| Length | As requirement |
| Finish | Acid Pickling , Polished , Unpolished , Mirror , HL , 180 Grit,400 Grit,600 Grit |
| Technical | Hot rolled , cold drawing , precision rolling |
| Standard | ASTM A312, ASTM A213, ASTM A269, ASTM A511 ASTM A789, ASTM A790 ,JIS3463, JIS3459, DIN2462, DIN17458, DIN17456 |
| MOQ | 5 ton |
| Certification | ISO 9001:2008 , MTC , PMI , CO , SGS |
| Shape | stainless steel round, square, rectangular, bending, oval seamless and welded pipe |
Specifications of stainless steel tube:
|
Feature: |
A) OEM,ODM orders are accepted; |
|||||
|
B) Best price; |
||||||
|
C) High quality; |
||||||
|
D) Prompt delivery; |
||||||
|
E) Manufacture according to the sizes and design of customers; |
||||||
|
F) Best service; |
||||||
|
G) Certification:ISO9001-2008 |
||||||
|
Our stainless steel tube an be bended to different shapes to suit for different designs and modeling in the construction work |
||||||
|
Material: |
Grade:201,202,304,316,430,etc. |
|||||
|
Different grade can meet different customer's requirement |
||||||
|
Product Specs: |
A:Round pipe |
|||||
|
12,13,14,16,19,25.4,31.8,44.5,50.8,63.5,76.2,etc. |
||||||
|
B:Rectangular pipe 10x30,10x40,10x50,10x75,10x80,10x90,10x100,20x40, 20x80,20x100,etc. |
||||||
|
25x38,25x50,25x75 etc. |
||||||
|
C:Single-slot pipe [external diameter X ( Slot depth X width )] |
||||||
|
25.4x(12x12),38.1x(15x15),42.4x(24x24),48.3x(27x30), 50.8x(15x15) |
||||||
|
50.8x(32x19),50.8x(38x19),60.3x(34x34),63.5x(20x20), 76.2x(25x25) |
||||||
|
D:Double-shot pipe [external diameter X ( Slot depth X width )] |
||||||
|
50.8x(15x15),63.5x(20x20),76.2x(25x25) |
||||||
|
E:Elliptical single slot pipe [external size X ( Slot depth X width )] |
||||||
|
40x80x(26x33),40x110x(26x33) |
||||||
|
F:Elliptical pipe |
||||||
|
20x38,23x38,20x40,28x46,38x62,42x75,40x80,40x110, 50x100,60x120 |
||||||
|
Length: |
standard is 6M,special length can be customized |
|||||
|
Production Capacity |
500 tons per month |
|||||
|
Application |
decorative /industrial/building material |
|||||
|
Min.bending radius: |
A:38.1~50.8=RX1M |
|||||
|
B:63.5~76.2=RX1.5-2.5M |
||||||
|
C:88.9~101.6=RX3-4.5M |
||||||
|
Production process: |
Turn on the roll -- solder side-forming -- weld -- weld the seam inner&external --polishing&fix melting -- fix the diameter&to be straight -- vortex test -- cuted by saw -- press test -- final test -- package |
|||||
|
Delivery time |
7-15days after order ,according to customer's order quantity. |
|||||
|
Packing: |
Every tube is sleeved in plastic bag individually, and then 10pcs/bundle or 50 pcs/bundle.We can pack as clients' requirement. |
|||||
|
Payment Terms: |
T/T 30% deposit,70% balance should be paid before shipment;L/C,D/P are available |
|||||
UNS S32707 is a hyper-duplex stainless steel, a high-alloy duplex steel with a PRE value of min. 48*. The grade is characterized by excellent chloride corrosion resistance, combined with very high mechanical strength.
S32707 is particularly suited for use in aggressive environments such as hot chlorinated seawater and for highly acidic, chloride containing media. S32707 has better resistance to pitting and crevice corrosion and higher mechanical strength than all super-duplex stainless steel grades available on the market.
*Besides bleow, we can supply comfortable price with equivalents quality for you! Welcome contact us.
>Marine engineering
>Furnaces&gas turbines
>Chemical processing plants
>Boiler & pressure vessels
>Nuclear power plants
| C | Si | Mn | S | P | Cr | Ni | Mo | Cu | N |
| max | max | max | max | max | |||||
| 0.03 | 1.00 | 1.50 | 0.02 | 0.035 | 26/29 | 5.5/9.5 | 4.0/5.0 | 1 | 0.3/0.5 |
| Property | Value | |
| Tensile Strength, min, ksi, [MPa] | 133 [920] | |
| Yield Strength, min, ksi [MPa] | 101 [700] | |
| Elongation in 2 in. or 50mm, min, % | 25 | |
| Hardness, max | HBW | HRC |
| 318 | 34 | |
Outsider Diameter OD : 6-630mm ; WT 3-60mm ; L max 16meter
Acid pickling - pre-passivation process of treating stainless steel parts with an acid solution, typically hydrochloric or sulfuric acid, which can remove oxide scale and heat tint while dissolving steel flecks embedded in the part.
Polishing - P grade sandpaper: P150, P200, P250, P300, P400, P500, P600, P700, P800
Chamical analysis / Tensile test at room temperature / flattening test / ring tensile test / drift expemdomg test / ring expanding test / leak tightness test / Tensile test at elevated temperature / impact test at room temperature / impact test at low temperature / eddy current test / ultrasonic test / magnetic flux leakage test
In addition to the marking prescribed in specification as client's request.
Bare / Nylon / Plastic / Wooden Case
General corrosion can limit the service life of a stainless steel component in contact with a process solution. S32707 is highly resistant to corrosion by organic acids,e.g.formic acid and acetic acid.It also remains resistant in contaminated acid.The alloy is,therefore,a competitive alternative to high alloyed austenitic stainless steels and Ni-base alloys in applications where standard austenitic stainless steels corrode at a high rate.
Stress corrosion cracking (SCC) is perhaps the most serious form of corrosion encountered in industrial processes as it can lead to rapid material failure.Standard austenitic grades can crack even at very low chloride levels.The risk of SCC can be eliminated with the use of more resistant
materials,such as high nickel alloys or duplex stainless steels.While the austenitic steels in many cases become resistant at Ni levels above 25%,the duplex alloys will have the same or higher resistance at much lower alloying levels,due to the dual phase structure .The SCC resistance of S32707 in chloride solutions at high temperatures is illustrated.An autoclave SCC test,where the samples are loaded to the yield strength R level,was conducted.The pressure was approximately 100 bar and the oxygen content 8 ppm.Fresh NaCl solution was pumped constantly into the chamber and duration of the test was 1000h (6 weeks).There were no signs of SCC up to 1000 ppm CI /300 C and 10000 ppm CI /250C.
In chloride containing waters under oxidizing conditions, pitting or crevice corrosion are perhaps the most common failure modes for stainless steels.Modern duplex stainless steels,such as 2507,were developed explicitly to have high resistance to pitting and crevice corrosion. All the experience gained from this grade has been utilized