1: Brief Introduction Of 420 stainless steel
Alloy 420 is a hardenable, martensitic stainless steel that is a modification of Alloy 410. Similar to 410, it contains a minimum
of 12% chromium, just sufficient enough to give corrosion resistant properties. Alloy 420 has higher carbon content than
Alloy 410 which is designed to optimize strength and hardness characteristics. It has good ductility it the annealed condition
but is capable of being hardened up to Rockwell hardness 50 HRC, the highest hardness of the 12% chromium grades. Due
to its hardening properties, Alloy 420 is not often welded, although it is possible. Martensitic stainless steels are designed for
high hardness and sometimes other properties are to some degree compromised. Corrosion resistance is lower than the
common austenitic grades and their useful operating range is limited by their loss of ductility at sub-zero temperatures and
loss of strength by over-tempering at elevated temperatures. Its best corrosion resistance is achieved when the metal is
hardened and surface ground or polished.
Corrosion Resistance:
*Less resistant than the austenitic grades and the 17% chromium ferritic alloys
*Good resistance in the hardened condition to the atmosphere, foods, fresh water, and mild acids
*Resistance lowered in the annealed condition
*Best with a smooth surface finish
Heat Resistance:
*Not recommended for use above the relevant tempering temperature because of reduction in mechanical properties
*Scaling temperature is approximately 1202oF (650oC)
Other Grades:
201,202,21-4N,301,302,301L,303,303Se,304,304L,304H,304LN,304N,305,S38400,308,309,309S,310,310s,
316,316L,316H,316Ti,316N,316LN,317,317L,317LMN,317LN,321,321H,347,347H,S3100,S31803,S3205,
S32304,S31200,S31260,S32507,405,409,429,430,430F,434,444,403,410S,410,416,420,420F,431F,440A
440B,440C,440F,610,630,631,632,635,660,Alloy 200,Monel 400 ,Alloy K-500 ,Inconel 600 , Incconel 601,
Inconel 625 , Inconel 718 , Alloy 800 ,Alloy 800H,Alloy 800HT,Inconel 825,Alloy 276, Alloy 20, Alloy 59
2: Chemical Composition
| Tianjin Zhongyantiancheng Steel Co.,Ltd |
| Commodity |
Stainless Steel Plate/Stainless Steel Sheet |
| Material |
420 |
| Standard |
GB |
JIS |
ASTM/ASME |
DIN |
| 2Cr13 |
SUS 420J1 |
420 |
1.4021 |
| Chemical Composition |
C |
Mn |
P |
S |
| ≥0.15 |
≤1.00 |
≤0.040 |
≤0.03 |
| Si |
Cr |
|
|
| ≤1.00 |
12.0-14.0 |
|
|
| Thickness |
0.3mm--16mm(cold rolled) 3mm--280mm(hot rolled) |
| Width |
1000mm--2200mm |
| Length |
1000mm-6000mm, as customers' request |
| Surface |
BA/2B/NO.1/NO.3/NO.4/8K/HL/2D/1D |
| manufacture |
Hot Rolled/Cold Rolled |
| Packing |
Packed in bundles with standard export sea-worthy package |
| Delivery Time |
Within 15 working days, according to customers' quantities |
| Quality |
High Quality.SGS inspection is accepted if needed |
| Place of Origin |
Jiangsu |
| Productivity |
500 MT/Month |
| Payment |
T/T,L/C |
| MOQ |
1 MT |
| Application |
Cuttery,Surgical instruments,Surgical instruments,Needle valves |
| Note |
We can also do other materials |
3: Stainless Steel Plate Process
4: Stainless Steel Plate Package
5: Company Introduction
.
Audited Supplier 
){kind=link}
){kind=link}