R30188 HS188 Alloy 188 AMS 5772 Haynes 188 Gh188 Alloy Bar

Product Description

UNS R30188 Alloy 188 AMS 5772 Haynes 188 gh5188 Gh188 High Temperature Alloy Bar

Shape	Round,Forging,Ring,Coil,Flange,Disc,Foil,Spherical,Ribbon,Square,Bar,Pipe,Sheet
Grade	Duplex: 2205(UNS S31803/S32205),2507(UNS S32750),UNS S32760(Zeron 100),2304,904L
	Others:253Ma,254SMo,654SMo,F50(UNSS32100)F60,F61,F65,1J22,N4,N6 etc
	Alloy : Alloy 20/28/31
	Hastelloy:HastelloyB/ -2/B-3/C22/C-4/S/ C276/C-2000/G-35/G-30/X/N/g
	Hastelloy B / UNS N10001,Hastelloy B-2 / UNS N10665 / DIN W. Nr. 2.4617,Hastelloy C, Hastelloy C-4 / UNS N06455 / DIN W. Nr. 2.4610,Hastelloy C-22 / UNS N06022 / DIN W. Nr. 2.4602, Hastelloy C-276 / UNS N10276 / DIN W. Nr. 2.4819,Hastelloy X / UNS N06002 / DIN W. Nr. 2.4665
	Haynes: Haynes 230/556/188
	Inconel 600/601/602CA/617/625/713/718/738/X-750,Carpenter 20
	Inconel 718 / UNS N07718 / DIN W. Nr. 2.4668,Inconel 601 / UNS N06601 / DIN W. Nr. 2.4851, Inconel 625 / UNS N06625 / DIN W. Nr. 2.4856,Inconel 725 / UNS N07725,Inconel X-750 / UNS N07750 / DIN W. Nr. 2.4669,Inconel 600 / UNS N06600 / DIN W. Nr. 2.4816
	Incoloy: Incoloy 800/800H/800HT/825/925/926;
	GH: GH2132,GH3030,GH3039,GH3128,GH4180,GH3044
	Monel: Monel 400/K500/R405
	Nitronic: Nitronic 40/50/60;
	Nimonic: Nimonic 75/80A/90/A263 ;
Specification	Wire: 0.01-10mm Strip: 0.05*5.0-5.0*250mm  Bar: φ4-50mm;Length 2000-5000mm Pipe: φ6-273mm;δ1-30mm;Length 1000-8000mm Sheet: δ 0.8-36mm;Width 650-2000mm;Length 800-4500mm

Introduction

Haynes 188 is a cobalt-based alloy which possesses a unique combination of properties. It has excellent high temperature strength and oxidation resistance to 2100°F (1150°C) combined with good post-aging ductility.
Alloy 188 has average room temperature tensile properties in the bright annealed condition of 137.2 ksi (946 MPa) ultimate strength, 67.3 ksi (464 MPa) yield strength and 53% elongation. At 1800°F (980°C) the alloy has ultimate and yield strengths of 35.2 ksi (243 MPa) and 19.0 ksi (131 MPa), respectively, with 59% elongation. Cryogenic temperatures do not significantly affect the ductility of alloy 188, but strength levels are increased markedly.
The excellent oxidation resistance of Haynes 188 results from minute additions of lanthanum, which modifies the protective oxide scale in such a manner that the oxide becomes extremely tenacious and retards diffusion when exposed to temperatures through 2100°F (1150°C).
Haynes 188 exhibits good ductility after prolonged exposure at temperatures of 1200, 1400, and 1600°F (650, 760 and 870°C) for 16,000 hours.
 

Chemical Composition

The chemical composition of Haynes 188 is outlined in the following table.

Element	Content (%)
Cobalt, Co	≥ 37
Nickel, Ni	22
Chromium, Cr	22
Tungsten, W	14
Iron, Fe	≤ 3
Manganese, Mn	≤ 1.25
Silicon, Si	≤ 0.50
Carbon, C	≤ 0.15
Lanthanum, La	0.040
Phosphorous, P	0.020
Sulfur, S	0.015

Physical Properties

The following table outlines the physical properties of Haynes 188.

Properties	Metric	Imperial
Density	8.9 g/cm^3	0.324 lb/in^3
Melting point	1330°C	2425°F

Other Designations

Other designations that are equivalent to Haynes 188 include:

• AMS 5608
• AMS 5772
• GE B50A712
• GE B50TF74
• GE B50TF74A

Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .

Q2: Can I have free sample before making orders?

A2: Yes,we can supply free sample as requirement,but buyer needs to pay the freight charges ,the freight fee will return to buyer after making order.

Q3: How do you control the quality ?
A3: MTC and PMI will be sent before shipment,any 3rd party inspection if need .

Q4: How about your delivery time ?
A4: Generally delivery time is 15 working days .

Q5: How can I quickly get the price list ?
A5: Directly click "chat now"  or send us email with detail specifications,you will get the official price list in 1 hour .