Industry Widely Cheap Prices Hastelloy G30 Nickel Based Alloy Rod for Sour-Gas Service Applications

• Customization: Available
• Application: Aviation, Electronics, Industrial, Medical, Chemical
• Standard: JIS, GB, DIN, ASTM, AISI
• Model NO.: Hastelloy G30
• Alloy: Alloy
• Type: Nickel Bar
• Powder: Not Powder
• Diameter: 3-300mm
• Surface: Black, Bright, Polished, Pickling
• Length: as Your Requirments
• MOQ: 100kgs
• Sample: Free-Sample
• Condition: Annealed;Heat Treatment
• Technique: Cold Rolled, Hot Rolled
• Mtc: Cold Drawn Hot Rolled,Forged
• Stock: in Stock
• T.S.(≥ MPa): 1096
• Key Words: G30 Alloy Supplier
• Transport Package: Wooden Package
• Specification: Hastelloy G30
• Trademark: ZYTC
• Origin: China
• HS Code: 7502200000
• Production Capacity: 50000kg/Month

Product Description

Black Hot Rolled Monel K500 Nickel Based Alloy Rod for Doctor blades and scrapers

Ni 46, Cr 30.0 Fe 15.0, Mo 5.5, W 2.5

Material	Monel/Inconel/Hastelloy/Duplex Steel/PH Steel/Nickel Alloy
Shape	Round,Forging,Ring,Coil,Flange,Disc,Foil,Spherical,Ribbon,Square,Bar,Pipe,Sheet
Grade	Duplex: 2205(UNS S31803/S32205),2507(UNS S32750),UNS S32760(Zeron 100),2304,904L
	Others:253Ma,254SMo,654SMo,F50(UNSS32100)F60,F61,F65,1J22,N4,N6 etc
	Alloy : Alloy 20/28/31
	Hastelloy:HastelloyB/ -2/B-3/C22/C-4/S/ C276/C-2000/G-35/G-30/X/N/g
	Hastelloy B / UNS N10001,Hastelloy B-2 / UNS N10665 / DIN W. Nr. 2.4617,Hastelloy C, Hastelloy C-4 / UNS N06455 / DIN W. Nr. 2.4610,Hastelloy C-22 / UNS N06022 / DIN W. Nr. 2.4602, Hastelloy C-276 / UNS N10276 / DIN W. Nr. 2.4819,Hastelloy X / UNS N06002 / DIN W. Nr. 2.4665
	Haynes: Haynes 230/556/188
	Inconel 600/601/602CA/617/625/713/718/738/X-750,Carpenter 20
	Inconel 718 / UNS N07718 / DIN W. Nr. 2.4668,Inconel 601 / UNS N06601 / DIN W. Nr. 2.4851, Inconel 625 / UNS N06625 / DIN W. Nr. 2.4856,Inconel 725 / UNS N07725,Inconel X-750 / UNS N07750 / DIN W. Nr. 2.4669,Inconel 600 / UNS N06600 / DIN W. Nr. 2.4816
	Incoloy: Incoloy 800/800H/800HT/825/925/926;
	GH: GH2132,GH3030,GH3039,GH3128,GH4180,GH3044
	Monel: Monel 400/K500/R405
	Nitronic: Nitronic 40/50/60;
	Nimonic: Nimonic 75/80A/90/A263 ;
Specification	Wire: 0.01-10mm Strip: 0.05*5.0-5.0*250mm  Bar: φ4-50mm;Length 2000-5000mm Pipe: φ6-273mm;δ1-30mm;Length 1000-8000mm Sheet: δ 0.8-36mm;Width 650-2000mm;Length 800-4500mm
Product  Characteristics	1.According to the preparation process can be divided into deformation superalloys,  casting superalloys and powder metallurgy superalloys. 2.According to the strengthening mode, there are solid solution strengthening type, precipitation  strengthening type, oxide dispersion strengthening type and fiber strengthening type, etc..
Standard	GB,AISI,ASTM,DIN,EN,SUS,UNS etc
Inspection	ISO,SGS,BV and so on.
Application	High temperature components such as turbine blades, guide vanes, turbine disks,  high pressure compressor disks,machine manufacturing and combustion chambers used in the manufacture of aviation, naval and industrial gas turbines
Packaging	1. cases packed in wooden cases 2. paper packaging 3. plastic packing 4. foam packaging Packaging according to customer requirements or products
Delivery	7-25days orAccording to the product
Payment	L/C,D/A,D/P,T/T,Western Union,MoneyGram,According to customer requirements payments for offline orders.

Overview

HASTELLOY G-30 is an improved version of nickel-chromium-iron molybdenum-copper alloy G-3. With higher chromium, added cobalt and tungsten the nickel HASTELLOY G-30 shows superior corrosion resistance over most other nickel and iron based alloys in commercial phosphoric acids as well as complex environments containing highly oxidizing acids such as nitric/hydrochloric, nitric/hydrofluoric and sulfuric acids. HASTELLOY G-30 resists the formation of grain boundary precipitates in the heat-affected zone, making it suitable in the as-welded condition.

HASTELLOY G-30 is basically the same as other high alloys in regard to formability. It is generally stiffer than an austenitic. Because of its good ductility, cold working is relatively easy and is the preferred method of forming. The alloy is easily weldable using Gas-Tungsten Arc, Gas Metal Arc and shielded Metal Arc. The welding characteristics are similar to those of G-3.

 

Machining

Nickel & cobalt base corrosion, temperature and wear-resistant alloys are classified as moderate to difficult when machining, however, it should be emphasized that these alloys can be machined using conventional production methods at satisfactory rates. During machining these alloys work harden rapidly, generate high heat during cutting, weld to the cutting tool surface and offer high resistance to metal removal because of their high shear strengths. The following are key points which should be considered during machining operations:

CAPACITY - Machine should be rigid and overpowered as much as possible.
RIGIDITY - Work piece and tool should be held rigid. Minimize tool overhang.
TOOL SHARPNESS - Make sure tools are sharp at all times. Change to sharpened tools at regular intervals rather than out of necessity. A 0.015 inch wear land is considered a dull tool.
TOOLS - Use positive rake angle tools for most machining operations. Negative rake angle tools can be considered for intermittent cuts and heavy stock removal. Carbide-tipped tools are suggested for most applications. High speed tools can be used, with lower production rates, and are often recommended for intermittent cuts.
POSITIVE CUTS - Use heavy, constant, feeds to maintain positive cutting action. If feed slows and the tool dwells in the cut, work hardening occurs, tool life deteriorates and close tolerances are impossible.
LUBRICATION - lubricants are desirable, soluble oils are recommended especially when using carbide tooling. Detailed machining parameters are presented Tables 16 and17. General plasma cutting recommendations are presented in Table 18.

 

RECOMMENDED TOOL TYPES AND MACHINING CONDITIONS
Operations	Carbide Tools
Roughing, with severe interruption	Turning or Facing C-2 and C-3 grade: Negative rake square insert, 45 degree SCEA1, 1/32 in. nose radius. Tool holder: 5 degree neg. back rake, 5 degree neg. side rake. Speed: 30-50 sfm, 0.004-0.008 in. feed, 0.150 in depth of cut. Dry2, oil3, or water-base coolant4.
Normal roughing	Turning or Facing C-2 or C-3 grade: Negative rate square insert, 45 degree SCEA, 1/32 in nose radius. Tool holder: 5 degree neg. back rake, 5 degree neg. side rake. Speed: 90 sfm depending on rigidity of set up, 0.010 in. feed, 0.150 in. depth of cut. Dry, oil, or water-base coolant.
Finishing	Turning or Facing C-2 or C-3 grade: Positive rake square insert, if possible, 45 degree SCEA, 1/32 in. nose radius. Tool holder: 5 degree pos. back rake, 5 degree pos. side rake. Speed: 95-110 sfm, 0.005-0.007 in. feed, 0.040 in. depth of cut. Dry or water-base coolant.
Rough Boring	C-2 or C-3 grade: If insert type boring bar, use standard positive rake tools with largest possible SCEA and 1/16 in. nose radius. If brazed tool bar, grind 0 degree back rake, 10 degree pos. side rake, 1/32 in. nose radius and largest possible SCEA. Speed: 70 sfm depending on the rigidity of setup, 0.005-0.008 in. feed, 1/8 in. depth of cut. Dry, oil or water-base coolant.
Finish Boring	C-2 or C-3 grade: Use standard positive rake tools on insert type bars. Grind brazed tools as for finish turning and facing except back rake may be best at 0 degrees. Speed: 95-110 sfm, 0.002-0.004 in feed. Water-base coolant.
Notes:
1 SCEA - Side cutting edge angle or lead angle of the tool. 2 At any point where dry cutting is recommended, an air jet directed on the tool may provide substantial tool life increases. A water-base coolant mist may also be effective. 3 Oil coolant should be premium quality, sulfochlorinated oil with extreme pressure additives. A viscosity at 100 degrees F from 50 to 125 SSU. 4 Water-base coolant should be premium quality, sulfochlorinated water soluble oil or chemical emulsion with extreme pressure additives. Dilute with water to make 15:1 mix. Water-base coolant may cause chipping and rapid failure of carbide tools in interrupted cuts.

 

RECOMMENDED TOOL TYPES AND MACHINING CONDITIONS
Operations	Carbide Tools
Facing Milling	Carbide not generally successful, C- grade may work. Use positive axial and radial rake, 45 degree corner angle, 10 degree relief angle. Speed: 50-60 sfm. Feed: 0.005-0.008 in. Oil or waterbase coolants will reduce thermal shock damage of carbide cutter teeth.
End Milling	Not recommended , but C-2 grades may be successful on good setups. Use positive rake. Speed: 50-60 sfm. Feed: Same as high speed steel. Oil or water-base coolants will reduce thermal shock damage.
Drilling	C-2 grade not recommended, but tipped drills may be successful on rigid setup if no great depth. The web must thinned to reduce thrust. Use 135 degree included angle on point. Gun drill can be used. Speed: 50 sfm. Oil or water-base coolant. Coolant-feed carbide tipped drills may be economical in some setups.
Reaming	C-2 or C-3 grade: Tipped reamers recommended, solid carbide reamers require vary good setup. Tool geometry same as high speed steel. Speed: 50 sfm. Feed: Same as high speed steel.
Tapping	Not recommended, machine threads, or roll-form them.
Electrical Discharge Machining	The alloys can be easily cut using any conventional electrical discharge machining system (EDM) or wire (EDM).
Notes:
5 M-40 series High Speed Steels include M-41 , M-42, M-43, M-44, M-45 and M-46 at the time of writing. Others may be added and should be equally suitable. 6 Oil coolant should be a premium quality, sulfochlorinated oil with extreme pressure additives. A viscosity at 100 degree F from 50 to 125 SSU. 7 Water-base coolant should be premium quality, sulfochlorinated water soluble oil or chemical emulsion with extreme pressure additives. Dilute with water to make 15:1 mix.