Black Finish Incoloy 800HT Nickel Based Alloy Bar for Pressure vessels
Incoloy 800, 800H, and 800HT are nickel-iron-chromium alloys with good strength and excellent resistance to oxidation and carburization in high-temperature exposure. These nickel steel alloys are identical except for the higher level of carbon in alloy 800H, and the addition of up to 1.20 percent aluminum and titanium in alloy 800HT. Incoloy 800 was the first of these alloys and it was slightly modified into Incoloy 800H. This modification was to control carbon (.05-.10%) and grain size to optimize stress rupture properties. Incoloy 800HT has further modifications to the combined titanium and aluminum levels (.85-1.20%) to ensure optimum high temperature properties. The nickel alloy is dual certified (800H/HT) and combines the properties of both forms.Incoloy 800H/HT alloy was intended for high temperature structural applications. The nickel content makes the alloys highly resistant to both chloride stress-corrosion cracking and to embrittlement from precipitation of sigma phase. The general corrosion resistance is excellent. In the solution annealed condition, alloys 800H and 800HT have superior creep and stress rupture properties. Today, most suppliers, including Mega Mex, only carry the dual certified 800H/HT alloy.
Incoloy 800 is primarily used in applications with temperatures up to 1100° F, where alloys 800H and 800HT are normally used in temperatures above 1100° F where resistance to creep and rupture is required. The chemical balance allows the nickel steel alloy to exhibit excellent resistance to carburization, oxidation and nitriding atmospheres. Incoloy 800HT will not become embrittled even after long periods of usage in the 1200-1600° F range where many stainless steels become brittle. Excellent cold forming characteristics typically associated with the nickel-chromium alloys are exhibited with 800HT. When cold formed extensively the grain size produces a visibly undulated surface called "orange peel". Incoloy 800HT can be welded by the common techniques used on stainless steels.
| Material | Monel/Inconel/Hastelloy/Duplex Steel/PH Steel/Nickel Alloy |
| Shape | Round,Forging,Ring,Coil,Flange,Disc,Foil,Spherical,Ribbon,Square,Bar,Pipe,Sheet |
| Grade | Duplex: 2205(UNS S31803/S32205),2507(UNS S32750),UNS S32760(Zeron 100),2304,904L |
| Others:253Ma,254SMo,654SMo,F50(UNSS32100)F60,F61,F65,1J22,N4,N6 etc | |
| Alloy : Alloy 20/28/31 | |
| Hastelloy:HastelloyB/ -2/B-3/C22/C-4/S/ C276/C-2000/G-35/G-30/X/N/g | |
| Hastelloy B / UNS N10001,Hastelloy B-2 / UNS N10665 / DIN W. Nr. 2.4617,Hastelloy C, Hastelloy C-4 / UNS N06455 / DIN W. Nr. 2.4610,Hastelloy C-22 / UNS N06022 / DIN W. Nr. 2.4602, Hastelloy C-276 / UNS N10276 / DIN W. Nr. 2.4819,Hastelloy X / UNS N06002 / DIN W. Nr. 2.4665 |
|
| Haynes: Haynes 230/556/188 | |
| Inconel 600/601/602CA/617/625/713/718/738/X-750,Carpenter 20 | |
| Inconel 718 / UNS N07718 / DIN W. Nr. 2.4668,Inconel 601 / UNS N06601 / DIN W. Nr. 2.4851, Inconel 625 / UNS N06625 / DIN W. Nr. 2.4856,Inconel 725 / UNS N07725,Inconel X-750 / UNS N07750 / DIN W. Nr. 2.4669,Inconel 600 / UNS N06600 / DIN W. Nr. 2.4816 |
|
| Incoloy: Incoloy 800/800H/800HT/825/925/926; | |
| GH: GH2132,GH3030,GH3039,GH3128,GH4180,GH3044 | |
| Monel: Monel 400/K500/R405 | |
| Nitronic: Nitronic 40/50/60; | |
| Nimonic: Nimonic 75/80A/90/A263 ; | |
| Specification |
Wire: 0.01-10mm Strip: 0.05*5.0-5.0*250mm Bar: φ4-50mm;Length 2000-5000mm Pipe: φ6-273mm;δ1-30mm;Length 1000-8000mm Sheet: δ 0.8-36mm;Width 650-2000mm;Length 800-4500mm |
| Product Characteristics |
1.According to the preparation process can be divided into deformation superalloys, casting superalloys and powder metallurgy superalloys. 2.According to the strengthening mode, there are solid solution strengthening type, precipitation strengthening type, oxide dispersion strengthening type and fiber strengthening type, etc.. |
| Standard | GB,AISI,ASTM,DIN,EN,SUS,UNS etc |
| Inspection | ISO,SGS,BV and so on. |
| Application |
High temperature components such as turbine blades, guide vanes, turbine disks, high pressure compressor disks,machine manufacturing and combustion chambers used in the manufacture of aviation, naval and industrial gas turbines |
| Packaging |
1. cases packed in wooden cases 2. paper packaging 3. plastic packing 4. foam packaging Packaging according to customer requirements or products |
| Delivery | 7-25days orAccording to the product |
| Payment |
L/C,D/A,D/P,T/T,Western Union,MoneyGram,According to customer requirements payments for offline orders. |
| Ni | Cr | Fe | C | Al | Ti | Al+Ti |
|---|---|---|---|---|---|---|
| 30.0-35.0 | 19.0-23.0 | 39.5 min | .10 max | .15-.60 | .15-.60 | .30-1.20 |
| Ni | Cr | Fe | C | Al | Ti | Al+Ti |
|---|---|---|---|---|---|---|
| 30.0-35.0 | 19.0-23.0 | 39.5 min | .05-.10 | .15-.60 | .15-.60 | .30-1.20 |
| Ni | Cr | Fe | C | Al | Ti | Al+Ti |
|---|---|---|---|---|---|---|
| 30.0-35.0 | 19.0-23.0 | 39.5 min | .06-.10 | .25-.60 | .25-.60 | 0.85-1.2 |
*Note that the chemical composition of Incoloy 800HT will always be within the limits of Incoloy 800H.
*Note the limits of Incoloy 800H may or may not be within the limits of Incoloy 800HT.
Alloys 800H/HT are used in a variety of applications involving exposure to corrosive environments and high temperatures such as heat treating equipment, chemical and petrochemical processing, nuclear power plants and the paper pulp industry. Heat-treating equipment such as baskets, trays, and fixtures employ Incoloy 800H/HT. Chemical and petrochemical processing industries use the alloys for heat exchangers and other piping systems in nitric acid media especially where resistance to chloride stress-corrosion cracking is required. Power plants use them for super-heater and re-heater tubing.
| Alloy | Pipe Smls | Pipe Welded | Tube Smls | Tube Welded | Sheet/Plate | Bar | Forging | Fitting | |
|---|---|---|---|---|---|---|---|---|---|
| Alloy 800 (UNS N08800) | B407 | B154 | B163 | B515 | B409 | B408 | B564 | B366 | |
| Alloy 800H (UNS N08810) | B407 | B154 | B163 | B515 | B409 | B408 | B564 | B366 | |
| Alloy 800HT (UNS N08811) | B407 | B154 | B163 | B515 | B409 | B408 | B564 | B366 |
Typical room temperature Tensile Properties of Annealed Material
| Product | Tensile (ksi) | .2% Yield (ksi) | Elongation (%) |
|---|---|---|---|
| Rod & Bar | 75-100 | 30-60 | 60-30 |