500mm Large Diameter 5083 Aluminum Round Bar Stock

• Customization: Available
• Shape: Round
• Application: Transportation Tools, Door & Window, Glass Wall, Heat Sink, Decorations
• Model NO.: 5052/5083
• Certification: RoHS, ISO9001, ASTM, JIS, GB, EN, ASTMB
• Technique: Extruded
• Grade: 5000 Series
• Temper: O - H112
• Surface Treatment: Mill Finish/Anodized
• Alloy: Non-alloy
• Diameter: 3mm-720mm
• Length: as Your Requirement
• Standard: ASTM B211
• Certificate: En 10204/3.1
• Delivery Time: Within 10-15 Working Days
• Technical Process: Extruded/Forged/Cold Drawn
• Keyword: 5083 Aluminum Bar
• Transport Package: Standard Export Sea Worthy Package
• Trademark: ZYTC
• Origin: China
• HS Code: 7604291090
• Production Capacity: 500 Tons/Month

Product Description

1: Brief Introduction Of 5083 Aluminium/Aluminum Round Bar  

5083 aluminium alloy is an aluminium alloy with magnesium and traces of manganese and chromium. It is highly resistant
to attack by seawater and industrial chemicals.
Alloy 5083 retains exceptional strength after welding. It has the highest strength of the non-heat treatable alloys, but is not
recommended for use in temperatures in excess of 65°C.
Annealing:
Aluminium / Aluminum 5083 alloy can be annealed at 343°C (650°F) and then cooled in air.
Cold Working:
Conventional methods work best for cold working Aluminium / Aluminum 5083 alloy.
Welding:
Aluminium / Aluminum 5083 alloy can be welded by conventional methods and the filter rod used is this process is of the
same alloy.
Forging:
Aluminium / Aluminum 5083 alloy can be forged in the temperature range of 454 to 399°C (850 to 750°F).
Forming:
Aluminium / Aluminum 5083 alloy has good forming characteristics when either cold or hot worked.
Machinability:
Conventional methods are used for the machining process of Aluminium / Aluminum 5083 alloy.
Heat Treatment:
Aluminium / Aluminum 5083 alloy is a non-heat treatable alloy.
Hot Working:
Aluminium / Aluminum 5083 alloy is hot formed at 204°C (400°F) or higher to 371°C (700°F) when severe deformation is
needed.
Hardening:
Aluminium / Aluminum 5083 alloy is hardened only by cold working.
Applications:
Aluminium / Aluminum 5083 alloy is used in missile components, welded pressure vessels, auto aircraft cryogenics,
TV towers, drilling rigs, transportation equipment and marine parts.

2:Chemical Composition 

The aluminum industry has created a system using a four-digit numerical designation to identify wrought aluminum
alloys.  The first digit indicates the major alloying element.  The second digit indicates whether there was a modification
in the basic alloy.  The third and fourth digit indicates the specific alloy.  The following represent the various groups:

1XXX	Aluminum 99% or greater
2XXX	Copper - major alloying element
3XXX	Manganese - major alloying element
5XXX	Magnesium - major alloying element
6XXX	Magnesium and silicon - major alloying elements
7XXX	Zinc -major alloying element

Aluminum Grades:
1000 series: 1035,1040,1050,1060,1070,1080,1090,1098,1100,1230,1435,1260,1170,1275,1285,1385
2000 series: 2001,2002,2011,2014,2017,2117,2218,2519,2024,2224,2025,2030,2031,2036,2090,2091
3000 series: 3002,3003,3004,3103,3203,3303,3105,3006,3007,3107,3008,3009,3015,3016
5000 series: 5005,5205,5006,5010,5013,5014,5016,5017,5040,5043,5050,5150,5251,5351,5451,5052,5083
                    5352,5552,5254,5754,5856,5456,5283
6000 series: 6101,6201,6003,6103,6105,6205,6006,6106,6110,6061,6060,6063,6863,6081,6082,6162,6863
7000 series: 7001,7003,7005,7108,7129,7146,7050,7472,7075,7076,7277,7178,7278,7091,7277
8000 series: 8001,8004,8006,8011,8111,8014,8030,8130,8177,8079,8081,8280,8091
3:Aluminium/Aluminum Alloy Bar Process 

4: Company Introduction