5454 aluminium alloy is an alloy in the wrought aluminium-magnesium family (5000 or 5xxx series). It is closely related to 5154 aluminium alloy. As an aluminium-magnesium alloy, it combines moderate-to-high strength with excellent weldability. Like 5154, 5454 aluminium is commonly used in welded structures such as pressure vessels and ships. As a wrought alloy, it can be formed by rolling, extrusion, and forging (although forging is not common), but not casting. It can be cold worked to produce tempers with a higher strength but a lower ductility. It is generally not clad.
Annealing:
Aluminium / Aluminum 5454 alloy is annealed at 343°C (650°F) only when the need to relieve the cold working stress arises. After being sufficiently heated the alloy is finally cooled in air.
Cold Working:
Aluminium / Aluminum 5454 alloy is capable of being cold worked by using conventional methods. This alloy can be cold worked in any of the H-32, H-34, H-111 tempers or in the annealed condition.
Welding:
Aluminium / Aluminum 5454 alloy is capable of being welded by all the commercial welding methods.
Forging:
Aluminium / Aluminum 5454 alloy can be hot forged.
Forming:
Aluminium / Aluminum 5454 alloy can be readily cold worked in the annealed or tempered conditions. This alloy contains good cold working and hot working characteristics.
Machinability:
The machinability of Aluminium / Aluminum 5454 alloy is rated from fair to poor. Machining operations for this alloy is recommended when the alloy is in the H-34 temper condition. Oil lubricants can be used in the machining process.
Heat Treatment:
Aluminium / Aluminum 5454 alloy cannot be heat treated.
Hot Working:
Aluminium / Aluminum 5454 alloy can be hot worked in the temperature range of 371 to 204°C (700 to 400°F).
Hardening:
Aluminium / Aluminum 5454 alloy can be hardened only by being cold worked.
Applications:
Aluminium / Aluminum 5454 alloy is used in pressure vessels, marine service and welded structures.
| 1XXX | Aluminum 99% or greater |
| 2XXX | Copper - major alloying element |
| 3XXX | Manganese - major alloying element |
| 5XXX | Magnesium - major alloying element |
| 6XXX | Magnesium and silicon - major alloying elements |
| 7XXX | Zinc -major alloying element |